US $1.56200 - 40,000 kilogram
US $1.0740,001 - 999,999 kilogram
Paramtents
Certification SGS,MSDS,RoHS
HARDNESS 18-40A
Mixing Ratio 2%
Type silicone rubber
Appearance Fluid
Application Mold making materials
Certificated RoHS, Reach, MSDS,SGS.ISO9001:2008
EINECS No 39100000
Purity 100%
Sample Free
Packging & Delivery
Min Order200 kilogram
Briefing
Detailed
Hongye Silicone Rubber IN China
Description of Hongye Silicone Rubber IN China:
725# Brushing silicon is mainly used for toy gifts and craftwork gifts with the advantages of good tensile strength, high tear strength, high temperature resistance, high duplication times and repeated use, etc. It is suitable for small products or fine and precision products which is difficult to demould. This brushing silicon is one of the products with the highest use level in the production of craftwork gifts and the shrinkage is up to 2‰.silicon applications: Poly technique, lightings, candles, and molds in multiple pieces for large products.
Hongye Silicone Rubber IN ChinaStandard Datasheet:
Model | Appearance | Viscosity (cps) | Hardness (A°) | Tensile strength (Mpa) | Tear strength (KN/m) | Elongation (%) | Mixing ratio(%) | Operating time(H) | Curing time(H) |
725 | White | ≤27000 | 25±2 | ≥3.0 | ≥20 | ≥380 | 2~3 | 0.5~1 | 2~5 |
General Description:
RTV-2 molding silicon rubber and brushing silicon are general called two-component room temperature vulcanization silicon rubber with excellent fluidity and good operational performance. Add curing agent of 2%-3% at the room temperature, the brushing silicon is still operational within 30 minutes,and in 2-5 hours, an elastic silicon mold will be obtained with resistance to deformation, high-temperature, acid and alkali and expansion. The brushing silicon is mainly applicable to mold duplication of poly crafts, resin craftworks, lightings, candles, etc. and fabrication of precision molds.
Operation Instruction for brushing silicon :
The brushing silicon is white or red flowing liquid with general hardness of 23—27A°after curing . If the customer wants to make large products and large size molds, the mold should be made of silicon rubber with high hardness. On the contrary, if the mold with fine and precision patterns , it should be made of silicon with low hardness. The amount of the curing agent depends on the actual requirements of the customer. If molds requiring fast drying and demould, more curing agent is needed; contrarily, if molds requiring slower drying and demould, less curing agent is needed.
(Note: our company does not recommend you to add silicone oil. If a special soft silicon mold or fine detailed and complex patterns products are required, 5%-10% silicon oil can be added to soften the mold for easy demould.)
The proportions and reactions of the curing agent and the brushing silicon are listed as follows:
1. Adding curing agent 1%, the silicon can still be operated within 2.5 hours and can be demoulded after 6-8 hours.
2. Adding curing agent 2%, the silicon can still be operated within 50 minutes to 1 hour and can be demoulded after 2-3 hours.
3. Adding curing agent 3%, the silicon can still be operated within 28 - 30 minutes and can be demoulded after 1.5-2 hours.
4. Adding curing agent 4%, the silicon can still be operated within 10 - 15 minutes and can be demoulded after 1 -1.5 hours.