Silicone rubber for shoe molding

Shoe mold silicone rubber TECHNICIAL DATASHEET

FEATURES:

Two-part silicon rubber: flowable liquid silicon and curing agent.

Cures at room temperature within 4-5 hours. An exceptional fluidity and good operability, easy to demold.

Good tensile and tear strength, low shrinkage.

Suitable for pourable                                                              

RTV

Liquid Silicon Rubber Series

RTV-2 Room temperature silicone rubber

Model:  620# 

Usage: Silicon rubber for PU/poly resin, unsaturated resin, plaster, candles and gypsums crafts, toys, soap, statuary ,casting molds making,etc.

Pictures for shoe mold silicone rubber:

Curing agent and silicon proportion and reaction(Under room-temperature-25C):
1,Added with 2% of curing agent, silicon can      still flow within 2.5 hours, mold can be released in 8-10 hours.
2,Added with 3% of curing agent, silicon can still flow within 1.1 to 1.2 hours, mold can be released in 6-8 hours.
3,Added with 4% of curing agent, silicon can still flow within 55-60 minutes, mold can be released in 4-5 hours.
4,Added with 5% of curing agent, silicon can still flow wtithin 45-50 minutes, mold can be released in 4-5 hours.

TECHNICAL GUIDELINES:

1. Stir the base (Part A) well beofre use (except when depending on machine ).

2. Shake the catalyst container (Part B) well before use.

3. This is a 100 Part A to 5 Part B mixing ratio by weight.Weigh the desire amount of base into a clean mixing container.

4. Weight the proper amount of catalyst into the container. Mix the base and catalyst together by stirring with a stick until a uniform color is obtained. Scrape the container walls and bottom well to insure a thorough mix.

5. Though it is often unnecessary to deair the material due to its low viscosity some may choose to do so. If so, place the container into a vacuum chamber and evacuate the entrapped air from the mixture using a vacuum pump capable of achieving 29 inches of mercury vacuum. The mixture will rise, crest and then collapse in the container. Interruption (bumping) of the vacuum may be necessary to prevent overflowing the container. Keep the mixture under full vacuum for 2-3 minutes.

6. Bleed air slowly into the vacuum chamber. When the chamber is at atmospheric equilibrium, remove the cover plate and take out the container.

7. Pour the deaired material slowly in a steady stream from one end of the mould so that the material flows evenly over the pattern. This should minimize entrapment of air bubbles under the flowing material. A ”ready” mold may be poured firstly over the pattern, which will also help reduce the possibility of entrapping air on the pattern and in the cured rubber. A mold release agent may be applied on the pattern first to improve release.

8. Allow the rubber to cure for 2-4 hours at 24C before removing the cured rubber mold from the pattern. Heat acceleration not recommended with this product.

9. For best results, allow the mold to air cure an additional 24 hours before using it in production.

SHELF LIFE: 

Twelve(12) months from date of shipment when stored at 250C in the original  sealed packages.

PACKAGE:

Packed in clean 25kg/pail, 200kg/pail.

For further infomation,pls do not hesitate to contact 