Polyresin Molding Silicone Rubber

Polyresin Molding Silicone Rubber is used for

- Unsaturated polyester resins, epoxy resins, polyurethane resins.

- Polyurethane elastomers.

- Natural and synthetic waxes, candle, soap.

- Plasters, gypsum, column, cornices, domes, cements, concrete .

- Low-melting point

- Imitation wood and bench.

Features of Polyresin Molding Silicone Rubber 

a. Hardness from 10 shore A to 60 shore A

b. Low viscosity good for casting pouring mold,add thickening agent,the silicone can be brushable with nice operation ability.

c. High temperature resistance,high duplication times

d. Excellent tear and tensile strength

f. Different catalyst with different pot life and curing time, you can according your products to choose the catalyst and the viscosity.

Polyresin Molding Silicone Rubber instruction

Add curing agent of 2% to 3% at the room temperature, the Polyresin Molding Silicone Rubber is still operational within 30 minutes, and in 3 hours.

1. Adding curing agent 1%, the Polyresin Molding SiliconeRubber can still be operated within 2. 5 hours and can be Demoulded after 8 hours.

2. Adding curing agent 2%, the Polyresin Molding Silicone Rubber can still be operated within 50 minutes to 1 hour and can Be demoulded after 3 hours.

3. Adding curing agent 3%, the Polyresin Molding Silicone Rubber can still be operated within 30 minutes and can bedemoulded after 2 hours.

4. Adding curing agent 4%, the Polyresin Molding Silicone Rubber can still be operated within 15 minutes and can be demoulded after 1. 5 hours.

Further information of RTV silicone for mold making, please feel free to Contact Ms. Apple