Paramtents
Product E-620
Appearance Translucent
Hardness(shore A) 20±2
Mix ratio(A:B) 1:1/10:1
Viscocity Part A(mPa.s) 23000±2000
Viscocity Part B(mPa.s) 3500±500
Tensile strength (kgf/cm2) 45±5
Tear-strength (kN/m) 20±2
Elongation(%) 500±50
Curing time/setting time (hrs) 3-4hrs(25℃) 110-20mins(60℃)
Packging & Delivery
Min Order200 kilogram
Briefing
Detailed
liquid silicone rubber for tire mold manufacturer
liquid silicone rubber for tire mold Description
HY- E series addition molding silicone is generally named two-component siliconerubber, Part A and part B. It features an exceptional fluidity and good operability.
The mixing ratio is 1:1 (10:1), mainly be suitable for making molds application.
liquid silicone rubber for tire mold Typical Applications
HY- E series addition molding silicone could be mainly used for making concretestones, wax molds, PU molds, resin molds, gypsum casting, candle molding andchocolate, candy and any other FDA food product mold making, prototyping etc.HY-E620 Silicone Rubber is has been used for years to make tire pattern molds.
liquid silicone rubber for tire mold Characteristics
*low shrinkage (less than 0.1%)
*high tensile and tear strength with high copy times
*easy for operation (mixing ratio at 1:1 /10:1)
*very good flow and easy for pouring operation
*Fast and non-shrink cure at room temperature which can be accelerated considerably by the application of heat
liquid silicone rubber for tire mold Technical Parameters
Product | E-620 |
Appearance | Translucent |
Hardness(shore A) | 20±2 |
Mix ratio(A:B) | 1:1/10:1 |
Viscocity Part A(mPa.s) | 23000±2000 |
Viscocity Part B(mPa.s) | 3500±500 |
Tensile strength (kgf/cm2) | 45±5 |
Tear-strength (kN/m) | 20±2 |
Elongation(%) | 500±50 |
Pot life/working time (mins) | 30-40 |
Curing time/setting time (hrs) | 3-4hrs(25°C) 110-20mins(60°C) |
Shrinkage rate (%) | 0.1 |
(Please note: the above data for this product in 25°C temperature, 55percent humidity conditions, for reference. The accurate data is measured by customers when using.)
Operation instruction of liquid silicone rubber for tire mold:
1. Pls clear the model and tool totally before operation to prevent cure inhibition.
2.Weigh the two part correctly by electronic weight in two separate container .
3. Mixing the two part in 1:1/10:1 and stir part A and part B evenly in 2-3 minutes .
4.And get the mixture for vacuum-pumping for de-air the bubble in around 2-3
minutes . (If there is no vacuum machine, pls pour the mixture carefully and slowly
down the side of the mold frame so that less bubbles caused)
5. Enclose the product (the original model) with four plastic plates or wooden plates.
6. Clean your products and brush a layer of release agent(detergent or soap water) on
your product.
7. Pour the vacuumed mixture into the model frame from the side of the mold frame .
liquid silicone rubber for tire mold Notice:
As our E-series silicone is platinum cure silicone , which is very easy to cause
cure inhibition , so pls do remember thoroughly clean the model and tool beforeoperation . Besides, pls avoid the liquid E-series silicone contact or mix with the
following material , otherwise the silicone won’t be cured :
1. Liquid condensation silicone (condensation silicone not completely cured or organic
tin compounds )
2 .Sulphur, sulfide and sulfur rubber materials.
3. Amine compounds as well as contains the amine materials.
4 .Pewter solder flux.
SHELF LIFE:
Twelve(12) months from date of shipment when stored at 250C in the original sealed packages.
PACKAGE:
Packed in clean 25kg/pail, 200kg/pail.
Any more information, pls feel free to contact Ms. Bella
Mobile: 0086-18938867572
Tel: 0086-755-89948006
Fax: 0086-755-89948030
Website: www (dot) szrl (dot) net
Email: hysi(at)szrl(dot)net
Skype: bellajiaqi
网络文化经营许可证:浙网文[2013]0268-027号|增值电信业务经营许可证:浙B2-20080224-1 2007-2024 Tradevv.com. All rights reserved.