Search This Supplers Products:Mold making Silicone rubberSilicone RubberLiquid Silicone rubberMolding Silicone RubberSilicone OilPad Silicone rubber
- Home
- About us
- Products
- RTV-2 silicone rubber for molds making
- Addition cure silicone rubber
- Life casting silicone rubber
- Liquid silicone rubber for insoles
- electronic potting silicone rubber
- injection moulding silicone rubber
- silicone foam
- Molding silicone rubber for tire molds
- Pad printing silicone rubber
- silicone rubber for textile coating& trademarks
- Other Silicone products
- Faqs
- News
- Certificate
- Contact us
transparent condensation silicone potting compound silicone rubber
- FOB Price
US $18.80200 - 40,000 kilogram
US $10.8040,001 - 999,999 kilogram
- group name
- electronic potting silicone rubber
- Min Order
- 200 kilogram
- brand name
- Hong Ye silicone rubber
- model
- HY-210 silicone oil,HY-210 transparet silicone rub
- Nearest port for product export
- Shenzhen, Guangzhou, Xiamen, Shanghai
- Delivery clauses under the trade mode
- FOB, CFR, CIF
- Acceptable payment methods
- T/T, L/C, Westem Union
- Export mode
- Export through agents
- update time
- Fri, 08 Nov 2013 19:14:54 GMT
Paramtents
Color transparent
Use For Molding
Certificated RoHS, Reach, MSDS,SGS.ISO9001:2008
Type silicone rubber
Appearance Fluid
Classification Chemical Auxiliary Agent
HS Code 3910 0000
Packging & Delivery
-
Min Order200 kilogram
Briefing
2.high quality
3.easy demould
4.light viscosity and no deformation
5.high-temperature resistance
Detailed
Name-transparent condensation potting compound
Number transparent condensation silicone potting compound silicone rubber
HY210 silicone rubber
Usage of transparent condensation silicone potting compound silicone rubber :
filling for LED,LCD electronic display,circuit board.
Description of transparent condensation silicone potting compound silicone rubber :
hy210 is condensation silicone potting compound in two parts with low viscosity.it can be cured completely at room temprature,hy210 works on the surface of material as PC(poly-carbonate)PP,ABS,PVC as to its superior bonding feature.it is also applicable for insulation ,waterproof and bonding of electronics parts.it meets the requirements of european rohs.
Typical application of transparent condensation silicone potting compound silicone rubber :
potting for protection of general electronic module.
ourdoor protection for LED screen.
Warm tips.
1.sealing pakage for storage,the mixture should be used up at once to avoid wasting.
2.silicone belongs to non-dangerous goods,but keep away form mouth and eyes.
3.when it gets stratified after a period of storage,please mix hy210 evenly before using.it does not affect the perfomance.
Package of transparent condensation silicone potting compound silicone rubber :
22kg/sed(part A 20kg + part B 2kg)
shelf life and transportation:
1.twelve (12) months when stored at 24 degree celsius in original unopened packages.
2.this kind of product is non-dangerous product,it can be transported as general chemicals.
3.products exceed the storage life should be confirmed normal before using.
technical guidelines of transparent condensation silicone potting compound silicone rubber :
1.pls put part A and part B in separate container and stir evenly before mixing the two-parts todether.
2.weight ratio/part A/part B=10:1
3.bubble release if necessary,deaeration the mixture under 0.08 mpa for 3 miutes.
4.hy210 is cured at room temperature,so pls put it under room temperature after pouring,it comes to next process when basically cured,and it takes about 24 hours for completely cured.
kindly note-----temperature and humidity with a tremendous influences for curing of hy210.
Technical parameters.
Properties index | Part A | Part B | |
Before Curing
| Appearence | Black fluid | Colorless/yellowish fluid |
Viscosisty(cps) | 2500±500 | - | |
Features when operation | Mixing Ratio(By weight) | 10/1 | |
Operating Time(25°C /min) | 20~30 | ||
Curing time(hr,basically cured) | 3 | ||
Curing time(hr,perfectly cured) | 24 | ||
Hardness(shore A) | 15±3 | ||
After Curing | Thermal Conductivity[W(m·K)] | ≥0.2 | |
Dielectric Strength(kV/mm) | ≥25 | ||
Dielectric permittivity(1.2MHz) | 3.0~3.3 | ||
Volume resistivity(Ω·cm) | ≥1.0×1016 | ||
Fire Resistance | 94-V1 | ||