Addtion Cure Silicone Rubber for Jewelry Casting Performance:
Addtion Cure Silicone Rubber for Jewelry Casting,Our E series rtv-2 addition cure mold making silicone is with the all the advantage of rtv-2 condensation cure silicone rubber, but is also featured with lower shrinkage and low viscosity, good fluidity; Without releasing any by-product with low molecular weight, and it's cured from top to bottom, from the inside and outside simultaneously, so it will be deeply-cured. The E sereise addition cure silicone will not meet the problem of degradation or sticky molds because of the existence of by-product of small molecules under certain conditions, (such as closed, high temperature).it's very suitable for all kinds of mold with a variety of sizes, shapes and large sized plaster, cement,ect molds making.
Addtion Cure Silicone Rubber for Jewelry Casting Main applications:
Addtion Cure Silicone Rubber for Jewelry Casting,This product can be used in not only the field of common RTV-2 moldmaking silicone. As the vulcanizing reactions of addition cure silicone is fundamentally different from tin cure silicone’s, it has no problem of deep vulcanize or reverse reaction, ect problem. Therefore, our addition cure silicone is particularly applicable for large stones, plaster and cement product replication. It features with lower viscosity, high strength , good fluidity, can also be very suitable for precision complex pattern of the original copy.
Technical Datasheets for Addtion Cure Silicone Rubber for Jewelry Casting
MODEL | COMPOUNENT | BEFORE CURING | AFTER CURING | ||||||
Appearance | A Viscosity cP(25°C) | B hardness (shore A) | C Pot life min(25°C) | D initial curing (h) | Tensil- strength (Mpa) | Tear- strength (kN/m) | Elongation (%) | ||
E635# | A+B | translucent | 30000±8000 6000±2000 10000±3000 | A+B (1:1) 35±2 | A+B (1:1) 30±10 | A+B(1:1) 3±1 | A+B (1:1) ≥4.0 | A+B (1:1) ≥7 | A+B (1:1) ≥200 |
E642# | A+B | translucent | 30000±8000 6000±2000 10000±3000 | A+B (1:1) 42±2 | A+B (1:1) 30±10 | A+B(1:1) 3±1 | A+B (1:1) ≥4.0 | A+B (1:1) ≥7 | A+B (1:1) ≥200 |
*E650# | A+B | translucent | 30000±8000 150±50 12000±3000 | A+B (10:1) 50±5 | A+B(10:1) 2±1Or | A+B(10:1,100°C) 20~30min | A+B (10:1) ≥4.0 | A+B (10:1) ≥7 | A+B (10:1) ≥200 |
Any further information, please feel free to contact Ms. Judy
MOBILE:086-18938867591
QQ: 18938867591
Skype: judy.zhao723
WEB: www dot szrl dot net
网络文化经营许可证:浙网文[2013]0268-027号|增值电信业务经营许可证:浙B2-20080224-1 2007-2024 Tradevv.com. All rights reserved.