Search This Supplers Products:Mold making Silicone rubberSilicone RubberLiquid Silicone rubberMolding Silicone RubberSilicone OilPad Silicone rubber
US $8.89100 - 40,000 kilogram
US $6.8940,001 - 999,999 kilogram
Paramtents
features high temperatrue resistance
certificates RoHS. MSDS.SGS ISO9001:2000
color white
Delivery Time within 3 days after payment confirmed in our bank.
Packaging Details 25kg/drum and 200kg/drum
mix 1:1 or 10:1
promotion over 500KG 2% discount
environmental protection yes
material liquid silicone with two part
usage liquid pad printing silicone rubber for plastics toys
Packging & Delivery
Min Order100 kilogram
Briefing
Detailed
pad printing silicone rubber:
Pad printing silicone rubber is mainly applicable to making pads for plastics toys , electroplating products, electronic toys, trademarks and irregular pattern printing. Pad printing pads is a carrier which transfer printing the patterns on the steel plate onto the toy products' surface.
pad printing silicone rubber:
pad printing silicone rubber with the advantages of abrasion resistance, high temperature resistance, good printing effect, etc., which made of top-quality raw material due to adding American Dupont Teflon high-temperature resistance new material, is processed through high-temperature machining.
pad printing silicone rubber datasheet:
Pad printing silicone rubber(HY-918)
Specifications:
Appearance: Yellow
Viscosity (CS): 20000~25000
Hardness (A): 28~30
Tensile strength (kgf /cm) ≥ 35
Tear-strength(kgf /cm)≥ 24
Elongation break: (%)≥ 400
Retractility (%): ≤ 0.3
Curing agent mixed rate (%): 2-3
Operate time (min): 30
Curing time (hours): 2-4
printing silicone rubber(HY-900)
Appearance: Yellow, red, green, white
Viscosity(CS): 20000~25000
Hardness(A): 28-30
Tensile strength (kgf/cm) ≥ 35
Tear-strength (kgf/cm) ≥ 24
Elongation break: (%)≥ 400
Retractility (%): ≤ 0.3
Curing agent mixed rate(%): 2-3
Operate time(min): 30
Curing time(hours): 2-4
Operation instruction forpad printing silicon rubber
Admixture amount of curing agent and silicon reaction:
1. Added with 1% of curing agent, silicon can still flow within 2.5 hours, mold can be released in6-8 hours.
2. Added with 2% of curing agent, silicon can still flow within 50 minutes to 1 hour, mold can be released in 2-3 hours.
3. Added with 3% of curing agent, silicon can still flow within 28-30 minutes, mold can be released in 1.5-2 hours
4. Added with 4% of curing agent, silicon can still flow within 10-15 minutes, mold can be released in 1-1.5 hours
5. Curing agent reaction rate is related with weather and temperature. Under 25 degree, they can be added according to the instruction or at double amount in winter or under subzero temperature.
(Note: Curing agent can not be added above the 4% maximum level and the normal proportion is 2%. If more than 4% is applied, the silicon will condensate too fast for normal usage).
Above is the mixing data for silicon and curing agent, the precise result of hundreds of times of our experiments. Provided that you arrange production according to our instruction, you are sure to manufacture first class products and maximize your profit this is not only the need of, but also our responsibility for and a satisfactory answer to our customers. We may not be the first, but we will try to be the best. The customers need is what we pursue!
Any question about pad printing silicone rubber, pls call Mr.wenson,
the tel is 86-755-88948294,
and the mobile phone is 18938867531